Hot dip galvanizing, also known as hot dip zinc, is the method of forming a layer of zinc coating on the surface of the workpiece after oil removal and rust removal, showing a clean and infiltrating surface, immediately immersed in the plating tank of zinc melting in advance. Cold galvanizing is the same after the removal of oil, in addition to lure, showing no pollution, infiltration of the workpiece hung into a special electroplating tank on the cathode, the anode with zinc. Switch on the DC power supply, zinc ions on the anode migrate to the cathode, and discharge on the cathode, so that the workpiece is coated with a layer of zinc layer hot dip galvanizing method.
There is no adhesion test of powder spraying or fluorocarbon spraying on packaged galvanized wire, but there are two points for reference: first, in sealed or air-free environment, non-metallic volatiles can corrode zinc coating; Second, zinc at higher than 230 degrees (c) will cause the matrix metal brittle. And powder spraying and fluorocarbon spraying are to be baked at a higher temperature and in a sealed environment, causing rapid corrosion of zinc, resulting in loose corrosion film resulting in coating adhesion decline, and even lead to (matrix) steel wire brittle situation may exist.
Galvanized hexagonal mesh uses: building wall fixed, heat preservation, heat insulation; Power plant piping, boiler heating; Anti-freezing, residential protection, landscaping protection; Raise chicken and duck, isolate chicken and duck house, play the role of protecting poultry; Protect and support seawalls, hillsides, roads and Bridges and other waterworks.
After the corrosion of impregnated hexagonal wire mesh, the original characteristics will be lost, and the shape, color and mechanical properties will be changed, resulting in equipment damage, pipeline leakage, etc., specifically, it is easy to break and lose the original protection function. Usually, there are three kinds of metal corrosion: physical corrosion, chemical corrosion, electrochemical corrosion, corrosion in addition to the chemical properties and organizational structure of the metal itself, but also related to the surrounding medium, such as wet environment is easier to rust than dry environment, more impurities than impurities less easy corrosion, high temperature conditions than low temperature conditions easy corrosion. After understanding these, we can effectively prevent the corrosion of impregnated six-sided wire mesh, prolong the service life of the product.
Galvanized wire to galvanized uniform, a body is now its cross section, the second is the longitudinal uniformity. In the actual operation process, such as the jitter of steel wire, the surface of the pot scum and other reasons will cause galvanized wire surface galvanized layer accumulation, should try to solve the problem.
Dip plastic six side barbed wire corrosion lost the original characteristics, in the shape, color and mechanical properties and other aspects will change, resulting in equipment damage, pipeline leakage, in particular, is prone to fracture, lose the original protective function.
As we all know, the mechanism of resistance to atmospheric corrosion of zinc includes mechanical protection and electrochemical protection. Under the condition of atmospheric corrosion, there are ZnO, Zn(OH)2 and basic zinc carbonate protective film on the surface of zinc layer, which to a certain extent slows the corrosion of zinc. When this protective film (also known as white rust) is damaged, a new film will be formed.
Appellation: Hook fence is a variety of guardrail. The diameter of the opposite side of each mesh is generally 6.5cm-14cm. The thickness of the wire used is generally from 3.5mm to 6mm. Wire material is generally Q235 low carbon wire. The wire is welded by gimmick into decorative hook mesh black. The general size of the net is 1.5 meters X4 meters, 2 meters X4 meters, 2 meters X3 meters. The general surface treatment is cold (electric) galvanized treatment. There are also hot dip galvanizing, dip plastic, spray plastic. But overall, 99 percent is cold (electric) galvanized.