3, reduce the bivalent iron ion in the plating aid used for hot plating wire, reduce the formation of zinc slag
It is best to use special columns to fix the barbed rope installation, because the standard column is not only beautiful shape and better protection effect.
The production of large rolls of galvanized wire iron can be divided into two categories, is directly from the iron ore after iron stroke exercise out of the metal, the composition of the ore is iron oxide, silica and other miscellaneous stone.
The hot dip galvanized hexagonal net is made of low carbon steel wire by mechanized braided welding and then by hot dip zinc treatment. Net color bright white, thick zinc layer, uniform mesh, mesh surface smooth, solder joint tensile resistance, high corrosion resistance.
The impregnated hexagonal wire mesh will lose its original characteristics after corrosion, and will change in shape, color and mechanical properties, resulting in equipment damage, pipeline leakage, etc., specifically, it is easy to break and lose the original protection function. Usually there are three kinds of metal corrosion: physical corrosion, chemical corrosion, electrochemical corrosion, corrosion in addition to the chemical properties and organizational structure of the metal itself, but also related to the surrounding medium, such as wet environment than dry environment easy corrosion, more impurities than impurities less easy corrosion, high temperature conditions than low temperature conditions easy corrosion. After understanding these, we can effectively prevent the corrosion of impregnated hexagonal wire mesh, prolong the service life of products.
Galvanized wire is divided into hot dip galvanized iron wire and galvanized iron wire according to the production process. It has the characteristics of high tensile strength, good softness, zinc layer uniformity, corrosion resistance, beautiful color, good smoothness, strong adhesion and corrosion resistance. Hot dip galvanizing has better protective properties than electric galvanizing, so it is an important protective coating for steel parts used in harsh working conditions.
If the zinc coating is good, but when the light comes out in 3% nitric acid, there is a dark shadow on the coating, and the film is brown when passivation occurs, which may be caused by foreign metal impurities such as copper or lead in the galvanized liquid. When there is a problem in the process of galvanizing, check the temperature and current density first, and then measure and adjust the content of zinc and sodium hydroxide in the bath through the analysis of the bath. Whether DPE levels are low can be determined by Hull cell test.
On the contrary, the denser the ion deposition, the better the quality of zinc layer. Under the condition that the surface zinc layer is dense and bright, the quality of zinc layer per unit area should reach 80g/m2, and the process parameters should be optimized as follows: current density is 16-20A /dm2, mass concentration of zinc sulfate solution is 500g/L, and pH value is 2.5-3.0.
③ The galvanized iron wire shall not be damaged when it is tightened. Large coils of galvanized wire are divided into hot dip galvanized and cold dip galvanized. Hot dip galvanized wire is dark in color, consumes more zinc metal, forms infiltration layer with the base metal, and has good corrosion resistance. Hot dip galvanized wire can be maintained for decades in outdoor environment. Cold galvanized production speed is slow, uniform coating, thin thickness, usually only 3-15 microns, bright appearance, poor corrosion resistance, generally a few months will rust.
3, reduce the bivalent iron ion in the plating aid used for hot plating wire, reduce the formation of zinc slag