Galvanized wire coating rough, passivation film is not bright, bath temperature is too high. If the cathode current density is too high, zinc content in the bath is too high or sodium hydroxide and DPE content is too low; Electroplating solution with solid particles or excessive foreign metal impurities, will lead to such problems. Solution: If the large roll galvanized wire to the above coating is rough, there may be solid particles in the plating solution. If the roughness of the part is severe, the current density may be too high.
If not packaged, then a car of blade thorn rope can not be loaded with many pieces, but also relatively occupied places and easy to be lost in the process of transportation. Each bundle of blade barbed rope is 50 bundles. After hydraulic compression, the volume is reduced and it is more convenient to load and unload. Forklift trucks can load and unload easily. In general, when exporting, the blade thorn rope will be packaged for sale, so that the volume occupied in the container is relatively small, which can be very easy to size and place will not take up much place.
After annealing, the wire will become soft, flexibility will increase, iron is a relatively active metal, and more active than hydrogen, so it is a good reducing agent. At room temperature, iron is not easy to react with oxygen, sulfur, chlorine and other non-metallic elements in dry air. Its production cost is lower, its use and scale are also relatively wide, and it has better protective function. Therefore, it is an important material for steel parts in strict working environment.
When galvanized wire is galvanized, it is generally necessary to pay attention to the following problems: the duration of the protective effect of galvanized wire is greatly related to the thickness of the coating. Generally speaking, in the dry main gas and in indoor use, the thickness of galvanized wire galvanized layer only 6-12 μm “, and in harsh environmental conditions, galvanized wire galvanized layer thickness needs 20μm “to B height up to 50μm”. Therefore, the environmental impact should be considered when choosing the thickness of galvanized layer. Galvanized wire in galvanized, pay attention to the above problems, can be well galvanized, to ensure the quality of galvanized wire.
As we all know, the mechanism of resistance to atmospheric corrosion of zinc includes mechanical protection and electrochemical protection. Under the condition of atmospheric corrosion, there are ZnO, Zn(OH)2 and basic zinc carbonate protective film on the surface of zinc layer, which to a certain extent slows the corrosion of zinc. When this protective film (also known as white rust) is damaged, a new film will be formed.
Large hexagonal mesh called stone cage net, is mainly used for mountain protection, hydraulic construction and so on. Small wire hexagonal mesh is used as a good material for breeding, will twist twist hexagonal mesh in the welded iron frame on the hexagonal mesh welding into chicken coop, pigeon cage, rabbit cage cage cage, hexagonal mesh is the best material for breeding with a net.
The application of electric welding net is more widely, at present it has replaced the use of other parts of the wire mesh, the cost of electric welding net is lower, the production speed is very fast, so it is very popular. Welding net galvanized before the need for processing is recrystallization annealing, because the welding net must maintain a no oxide and no other impurities of pure iron active surface, if you can not keep its surface clean will lead to a bad galvanizing effect, galvanized layer and iron material is not closely combined, so this step is necessary.