During this process, each time the wire is pulled over, the surface hardens due to the high friction temperature. So basically every time you pull it you have to annealing it in the furnace. On the one hand, it is to reduce the surface hardness. On the other hand, during the process of wire pulling, only the surface is deformed, and the center is unchanged. So there’s a lot of stress inside. Therefore, it is necessary to rely on annealing to eliminate the internal stress, so that the wire becomes soft again to eliminate the stress before being drawn again.
Thus, when zinc is sufficient in a solid melt, the two atoms of zinc and iron disperse with each other. The zinc atoms in the iron matrix are moved into the lattice of the matrix, and the iron elements are gradually formed into alloys. The zinc composition of iron and intermetallic compound FeZn13 in molten zinc solution and the bottom of hot galvanized sheet can be used as zinc slag. The pure zinc layer composed of zinc leaching solution is hexagonal crystal.
Now the pet cage on the market is still mainly wire cage, so the identification of wire cage mainly has the following parameters:
A part of the customers always think that if the price is low to buy the barbed rope products, but often this time to buy the product quality or weight is not up to standard.
The main difference is carbon content. Iron has a carbon content of 2.11 percent or more, while steel has a carbon content of 2.11 percent or less. Iron-carbon alloys with carbon content of more than 2.11% are cast iron (pig iron), which are basically not malleable and cannot be drawn into wire. Secondly, the content of impurities is different, and the content of harmful impurities such as sulfur and phosphorus in steel is smaller. Wire general color key, wire color light point, white point.
2. The cleaning agent used for cleaning should have no effect on the binding force of the coating and no corrosion on the matrix.
Hot dip galvanizing, also known as hot dip galvanizing, is a method of obtaining a metal covering layer by immersing a steel member into a molten zinc solution. With the rapid development of high-voltage power transmission, transportation and communication, the protection requirements for steel parts are becoming higher and higher, and the demand for hot-dip galvanizing is also increasing. Usually the thickness of electrogalvanized layer is 5 ~ 15μm, and the large roll galvanized wire layer is generally more than 35μm, or even up to 200μm. Hot dip galvanized coating ability is good, dense coating, no organic inclusions.
There are many categories of large coils of galvanized wire, and different categories can be applied to different scenarios. Galvanized iron wire common application is the application of the construction industry, one is the use of binding wire, whether it is the binding of scaffolding or reinforcement, need galvanized iron wire to carry out, the common specifications are 22 and 24 wire, common length of 30cm, 35cm, 40cm, 45cm, 50cm. There is also 20kg or 50kg a bundle of 18, 16, 14, 12, 10 galvanized coil wire.
The main difference is carbon content. Iron has a carbon content of 2.11 percent or more, while steel has a carbon content of 2.11 percent or less. Iron-carbon alloys with carbon content of more than 2.11% are cast iron (pig iron), which are basically not malleable and cannot be drawn into wire. Secondly, the content of impurities is different, and the content of harmful impurities such as sulfur and phosphorus in steel is smaller. Wire general color key, wire color light point, white point.
The temperature of large roll galvanized wire should be controlled at 30 to 50℃ during electroplating. Because the chloride ions in the bath are very corrosive, quartz glass heaters are generally used. Continuous production does not need heating, but needs cooling. Cooling can be in the groove side row thin wall plastic pipe, through the flow of tap water cooling, can also be used as a titanium pipe temperature control device.
Cold galvanized by electrolytic action to metal and other materials surface attached to a layer of metal film, so that the surface of the material uniform texture, anti-corrosion wear, appearance is more beautiful. Hot dip galvanized coating is thicker, generally 30-60 microns, coating corrosion resistance is higher. Suitable for outdoor work of steel parts, such as highway fences, power towers, large size fasteners and other “rough” workpiece long-term rust prevention.
After the wire mesh appears black spots, you can choose the appearance of treatment to deal with this problem, such as galvanized, paint, dip plastic to deal with, after the appearance of the welding mesh surface smooth and bright, beautiful and generous.Cooling can be in the groove close row of thin wall plastic pipe, through the flow of tap water for cooling, can also be used as a temperature control device titanium pipe. In the process of electroplating galvanized wire, it is necessary to stir the plating solution to obtain the composite coating with particles dispersing in the matrix metal. Stirring methods include mechanical stirring, air stirring, ultrasonic stirring, bath circulation, etc.
Speaking of pets, we have to talk about parrots. Because it’s easy to take care of, and it can talk, talk to you, and make you laugh. Parrots love to climb, so there is a cage with bars that are made up of horizontal bars rather than vertical bars, because this makes climbing easier for the parrots.
Zinc adhesion on galvanized wire surface and thickness of zinc layer
The different spacing of the thorn rope is mainly in order to save costs to consider, because if they are too close, then obviously a little waste of resources, but the installation is too sparse will not work. Usually the bottom spacing is about 10cm, and the top is up to 20cm, this is because the higher the place is more difficult to climb over, usually more than one meter without the help of tools it is difficult for ordinary people to climb over, and the bottom because of the relatively tight can prevent personnel from drilling in the past.
The external environment has great influence on the preservation of galvanized wire mesh. In the rainy season, it is necessary to pay attention to the air humidity of the workshop, warehouse and other departments. It is recommended to use a humidifier. Usually, the moisture absorption of book paper is larger than that of powder paper, and the pH value is higher. Generally speaking, in the normal environment of storage wire, storage time of two years is not corroded wire phenomenon. However, it should be noted that in the process of handling the iron wire, it should be handled gently to avoid the position of the coiling coil, which will cause the smooth pulling of the wire and affect the production.
Product features: hot dip galvanized electric welding mesh surface flat, uniform mesh, straight warp and weft wire, diagonal accuracy within 3-5 mm. The structure of the net surface is strong, strong integrity, with strong corrosion resistance, beautiful, wide use and other characteristics. In white iron, its carbon and iron together into iron carbide, crack appears white, very strong and brittle quality, for the material of malleable steel. The alloy grade consists of various alloying elements with different compositions and structures. Because alloying elements in iron ore can make copper through the material thickening degree of strengthening, hardness, impact force, strength resistance, closing rate, elongation, so alloying iron in the exercise of high quality iron, is the primary supplementary element. Cold galvanized is in the plating tank through the current unidirectional zinc gradually plated on the metal surface, the production speed is slow, uniform coating, thin thickness, usually only 3-15 microns, bright appearance, poor corrosion resistance, generally a few months will rust. With the rapid development of market economy, all walks of life are improving the production process and quality of products, galvanized iron wire industry is of course no exception. But because of the variety of galvanized iron wire, its characteristics and production technology are not the same.