Hot dip galvanizing is dipped in zinc liquid melted by heating, with fast production speed and thick but uneven coating. The market allows a low thickness of 45 microns and a high of more than 300 microns. The color is dark, the consumption of zinc metal is much, the formation of infiltration layer with the matrix metal, the corrosion resistance is good, and the outdoor environment of hot dip galvanized can be maintained for decades. Application range of hot dip galvanizing: because the coating is thicker, hot dip galvanizing has better protective performance than electric galvanizing, so it is an important protective coating for iron and steel parts in harsh working environment. Hot-dip galvanized products are widely used in chemical equipment, petroleum processing, Marine exploration, metal structure, power transmission, shipbuilding and other industries, in the field of agriculture such as sprinkler irrigation, greenhouse and construction industry such as water and gas transmission, wire casing, scaffolding, Bridges, highway guardrail and other aspects, has been widely used.
Galvanized wire A stable layer of zinc is coated on the outside of the wire, which is used to protect the wire and make the wire service life longer. When producing galvanized wire, the wire is pickled. Pickling is to use some acid mist or acid to wash off some oxides on the surface of iron, that is, rust, and some other corrosive substances, to achieve the purpose of cleaning iron, so that zinc will fall off when galvanizing.
Steel wire mesh by its own unique advantages in construction occupation, reinforcement anti-crack occupation is indispensable reinforcement anti-crack data, high product error is small, mesh mesh uniform, welding firm, strong acceptance, not easy to deformation, steel wire mesh in different fields have different called, in bridge engineering construction people call it soft reinforcement.
Galvanized hexagonal net uses: building wall fixing, heat preservation, heat insulation; Power plant piping, boiler insulation; Anti-freezing, residential protection, landscaping protection; Raise chickens and ducks, isolate chicken and duck houses, protect poultry; Protect and support seawalls, hillsides, roads, Bridges and other water and wood works.
Large roll galvanized wire is made of low carbon steel wire rod processing, is made of low carbon steel, after drawing forming, pickling rust removal, high temperature annealing, hot dip galvanized. Cooling and other surface treatment process processing. Large roll galvanized wire is divided into hot dip galvanized wire and cold galvanized wire (electric galvanized wire). Although galvanized galvanized wire and silver powder paint spray effect appearance is not much different. But the effect is very different, galvanized wire surface is zinc layer, good adhesion, good corrosion resistance.
Under any application environment, users hope that the welding mesh has better strength, as long as it has improved in strength, it will make better use of the demand, but to make the strength of this product improve, also need to have many conditions, to see what kind of data manufacturers have in production, the strength of the product is the strength of the data, But a manufacturer does not meet the strength requirements in the data, and naturally, it cannot make the strength of the product improve after all, so this is the condition.
In reinforced concrete structure, the crack width of cold wire drawing is smaller than that of circular steel bar or even that of hot rolled thread bar. So cold wire drawing is more popular in the construction industry. The material for cold drawing is made of steel bars and can be simply explained how it is made, that is, its production process is simple. It’s based on steel bars, which are constantly stretched evenly, stretching the bars into something very thin, like wire drawing, without plasticity.
In the process of composite electroplating galvanized wire, the plating solution must be stirred to obtain the composite coating in which the particles dispersed in the matrix metal. Stirring methods include mechanical stirring, air stirring, ultrasonic stirring, bath circulation, etc. The acid activation solution in the production process can remove the corrosion products and oxide film on the surface of the low carbon steel wire without excessive corrosion on the matrix.