If the zinc coating is good, but in 3% nitric acid when the light, the coating has dark shadow, passivation occurs when the film is brown, may be caused by foreign metal impurities such as copper or lead in the galvanizing liquid. When problems occur in the process of galvanizing large coil galvanized wire, the temperature and current density are checked first, and then the content of zinc and sodium hydroxide in the plating solution is measured and adjusted through the analysis of the plating solution. Whether DPE content is low can be determined by hull cell test.
Remind you to buy galvanized iron wire, should be stored in dry, good ventilation conditions, do not contain corrosive gases, do not mix with the production of organic volatile gas paint, plastic and other substances in a good environment. If conditions, for galvanized parts to increase reliable inner packaging, and put desiccant. If the zinc layer white spots and hair, only mechanical removal, and then normal passivation, or thoroughly washed off the zinc layer after re-plating.
In GENERAL, THE HARDNESS OF A METAL IS OFTEN CONSIDERED AS THE RESISTANCE OF a MATERIAL TO COMPRESSION PLASTIC deformation, scratches, wear, or cutting. In the adjustment of zinc dip distance of galvanized wire, keep the original speed unchanged, according to the time of zinc dip, wire diameter, and then estimate the zinc dip distance. By adjusting the zinc dipping distance, the zinc dipping time of various specifications of steel wire is shortened by 5s on average compared with that before debugging, so that the zinc consumption is reduced, the zinc consumption per ton of steel wire is reduced from the original 61kg to 59.4kg.
For the specification of galvanized wire, the galvanized wire produced by our factory can range from No.8 to No.22, which refers to the BWG standard, that is, from about 4mm to 0.7mm, which can basically cover the type required by customers. As for the raw material of galvanized wire, normally, we use Q195 mild steel, and some factories will also use SAE1006 or SAE1008. The following is the zinc coating, for galvanized wire, this thing is more important, the general zinc coating is about 50g/m2 to 80g/m2, some customers need high zinc galvanized wire, zinc coating can reach 200g/m2 to 360g/m2. The tensile strength of galvanized wire is usually 350n/m2 to 800n/m2. Then there is the packaging specification of galvanized wire. The specifications of small rolls of galvanized wire are 50kg/ roll, 100kg/ roll and 200kg/ roll. Of course, there are large rolls of galvanized silk, the weight can reach 300kg/ roll or 800kg/ roll.
Carbon spring steel wire should have high tensile strength, elastic limit, endurance and fatigue strength, and impact and vibration resistance. To ensure the strength and endurance index, especially to avoid changing the occurrence of cracks, is the key to produce spring steel wire. The inner quality and surface quality of the wire rod directly affect the function of the wire.
With the development of mining industry, pig iron classification in Our country has been very extensive, can satisfy the demand of machinery industry. In general, iron used to produce large coils of galvanized wire can be divided into two classes. A metal produced directly from iron ore and iron smelting, consisting of iron oxide, silicon dioxide, and other miscellaneous stones. When this ore is specially refined into metal iron, carbon, silicon, manganese, and other elements are mixed in, so that the refined material is called general pig iron, is also for the initial grade of the material.
The formation process of hot dip galvanized layer is between the iron matrix and the outside of the pure zinc layer, the formation of iron-zinc alloy process, the workpiece surface in hot dip plating when the formation of iron-zinc alloy layer, so that the iron and pure zinc layer is well combined. The process of large roll galvanized wire can be simply described as: when the iron workpiece is immersed in the molten zinc liquid, the first zinc and α-iron (body-centered) solid melt is formed on the interface. This is a crystal formed by the matrix metal iron dissolved with zinc atoms in the solid state. The two metal atoms are fused with each other, and the attraction between the atoms is relatively small.
Annealed wire is a soft iron wire made of low carbon steel cold drawing, heating, constant temperature, heat preservation and other processes. The composition of iron wire varies according to its use. It contains iron, cobalt, nickel, copper, carbon, zinc, and other elements. The hot metal billet rolled into 6.5mm thick steel bar is the wire rod, and then put it into the wire drawing device into a different diameter of the line, and gradually reduce the aperture of the wire tray, cooling, annealing, plating and other processing technology made of various specifications of iron wire.
Plastic coated welding net: PVC plastic coated welding net is a kind of tall appearance of the welding net, plastic coated welding net picture upper protective barbed net, cable for galvanized steel wire, PVC coated plastic treatment, in the protection of beautiful at the same time, to ensure the strong and durable. Material: low carbon steel wire, PVC coated plastic manufacturing process: steel wire welding coated plastic, can also be separate plating, hot plating and coated plastic. PVC coated plastic welding net uses: industrial, agricultural, municipal, transportation and other industries fence, decoration, protection and other facilities.
3. Zinc layer structure: The structure of zinc layer includes grain size, grain shape and the combination of zinc layer and substrate, etc., which has a certain impact on corrosion resistance. In general, the finer the grain size, the denser the structure, and the better the corrosion resistance.