At present, there are two main kinds of electric galvanized wire products, hot dip galvanized wire and electric galvanized wire. The difference is that the way of galvanizing is different, and the quality of the products is different. Hot dip galvanized wire zinc layer thick, corrosion resistance is stronger, but correspondingly, the price is high. Galvanized wire zinc coating thin, corrosion resistance is poor, but the price is low.
In the atmosphere containing carbon dioxide and hydrogen sulfide and Marine atmosphere is not corrosion resistant, in high temperature and high humidity air and contain organic acid atmosphere is small, galvanized layer is also easy to be corroded. In order to make large rolls of galvanized wire on the surface of the deposited layer to the local, remove the surface film layer, surface inclusions and other defects can be found and treated by conventional techniques. Excess foam is caused by soaps and surfactant saponable fats brought into the tank, and moderate rates of foam formation may be harmless.
The wire rod should be normalized or soxhlet processed, instead of spheroidal annealing for standard large ones. Soxhlet process is widely used in the heat treatment of the center, especially the products before drawing. Avoid decarbonization during heat treatment. After heat treatment, sulfuric acid or hydrochloric acid pickling is used to remove iron sheet. The coating (see smooth carrier) can be dip-lime, phosphating, borax treatment or copper plating.
The entire steel surface is protected, and the melted zinc is easily coated evenly, whether in the interior of the pipe fitting in a depression, or in any other corner where the coating is difficult to access. The hardness of galvanized coating is greater than that of steel. The Eta layer of the upper layer of Z is only 70 DPN hardness, so it is easy to be dented by collisions. However, the hardness values of the lower layer of Zeta layer and delta layer are 179 and 211 DPN respectively, which are higher than that of the iron material of 159 DPN. Therefore, its impact resistance and wear resistance are quite good.
Hot dip galvanizing is to make the molten metal react with the iron matrix to produce an alloy layer, so that the matrix and the coating are combined. Hot dip galvanizing is to first pickling the iron and steel parts. In order to remove the iron oxide on the surface of the iron and steel parts, after pickling, it is cleaned in the tank of ammonium chloride or zinc chloride aqueous solution or mixed aqueous solution of ammonium chloride and zinc chloride, and then sent into the hot dip plating tank. Hot dip galvanizing has the advantages of uniform coating, strong adhesion and long service life.