Steel wire after galvanized treatment, the surface will be covered with a layer of zinc metal, to play the role of anti-corrosion, anti-fouling, enhance strength and beauty. The galvanized wire drawing treatment is to process the steel wire by stretching method to obtain a finer, higher strength and smoother surface, and improve its mechanical properties. However, will wire drawing affect the electrical conductivity of galvanized steel wire?
The use of galvanized anticorrosion treatment is better, the metallurgical connection between galvanized layer and steel, combined with the appearance of steel as a whole, making the coating more durable, more reliable. In the suburbs, the galvanized thickness of hot dip galvanized can adhere to more than 50 years without repair, in the suburbs or near the seaside, galvanized layer can adhere to more than 20 years without repair, is the choice of anti-rust and anti-corrosion. Coating has strong toughness, in the process of transportation or use, can resist extrusion, withstand some damage, hot dip galvanized anticorrosion treatment both save time and effort, and faster than other processing, than dipping, spraying to save much time and effort.
Large hexagonal net is called stone cage net, mainly used for mountain protection, hydraulic construction, etc. Small wire hexagonal net is used as a good breeding material, the twisted flower hexagonal net in the welding of the iron frame get on the hexagonal net burning welding coops, pigeonholes, rabbit cages and other cage, hexagonal net is the best breeding material with the net.
Galvanized iron wire can be divided into hot-dip galvanized iron wire and cold galvanized iron wire according to different processing methods. Galvanized iron wire is more prominent in its corrosion resistance. Galvanized iron wire has good toughness and elasticity, the amount of zinc can reach 300 g/square meter, with thick galvanized layer, strong corrosion resistance and other characteristics. Galvanized iron wire products are widely used in construction, handicrafts, wire mesh preparation, the production of galvanized hook mesh, wall mesh, highway guardrail, product packaging and daily civilian and other fields.
Therefore, when the zinc reaches saturation in the solid melt, the two elements of zinc and iron atoms are diffused with each other, and the zinc atoms diffused into (or infiltrated into) the iron matrix migrate in the lattice of the matrix and gradually form an alloy with the iron, while the iron diffused into the molten zinc liquid forms an intermetallic compound FeZn13 with the zinc and sinks into the bottom of the hot galvanized pot, that is, zinc slag. When the workpiece is removed from the zinc leaching solution, the surface of the pure zinc layer is formed, which is hexagonal crystal, and its iron content is not more than 0.003%.