If the coating roughness is not caused by the above reasons, it may be caused by impurities in the plating solution. Can take a small amount of electroplating solution, filtration test, and then take a small amount of electroplating solution, with zinc powder treatment after the test, check the problem is solid particles or copper, lead and other foreign metal impurities caused by. One by one, it’s not hard to find the cause of the problem. Galvanized iron wire coating blister, poor adhesion.
The type of barbed rope is mainly reflected in the specification of the wire diameter, the thicker the diameter of the barbed rope produced is shorter, at the same time, the price is cheaper, mainly because the production efficiency is relatively high, because the price of the barbed rope is calculated according to the weight when it is sold. On the contrary, the finer the diameter of the wire, the longer the price is higher.
Paint on the galvanized layer, the binding force between each other and the baking temperature of the paint has a great relationship, after galvanized coating alkyd paint, adhesion is no problem. Galvanized amino paint, paint adhesion is not good. Do two bottom two surface, adhesion is ok, if the two bottom two surface to two bottom three surface, that is, more paint, more baking once, again test adhesion is very poor, poor to the paint from the galvanized layer of pieces torn off.
2. Use a large pickpocket to stir the zinc ash before the steel wire enters the zinc liquid; Use a small outlet for the galvanized steel wire; Zinc pot steel wire outlet in 30 minutes, with pickpockets back and forth, until the large, floating zinc residue into brown, real zinc ash, zinc ash surface. After the removal of zinc ash should be brown yellow real zinc ash, zinc surface, effectively reduce zinc consumption. This is one of the measures to reduce zinc consumption, but it is also a real problem, which has not been solved for many years.
The quality of hot-dip galvanized barbed wire is only good in the surface of the wire attached to the galvanized layer, and with the chemical reaction, the surface of the zinc layer will gradually lose effect because of the oxidation reaction, this situation is more prominent in the humid area of the environment. And because after all, it is rusty iron wire, so the quality of hot-dip galvanized barbed rope is certainly not up to the level of stainless steel barbed rope.