Some large roll galvanized wire products in order to meet different industrial needs, will be further processed on the surface, such as the anti-corrosion layer, galvanized, iron plating, aluminum alloy plating, or in the galvanized wire appearance above the copper plating, brass plating, etc., to strengthen the steel wire and colloidal years and capabilities. Generally, galvanized wire products should be well plated and drawn when they are produced, and the sequence of the two processes should be decided according to the production or industrial needs.
High quality galvanized wire in general, the zinc layer attached to the surface of the wire is relatively thick, so when we buy galvanized wire, as long as we look at the thickness of the zinc layer machine, we can generally judge whether the quality of galvanized wire is high quality.
Galvanized iron wire is divided into hot galvanized wire and cold galvanized wire, using low carbon steel wire processing, after drawing molding, pickling rust removal, high temperature annealing, hot galvanized, cooling and other processes. It has good toughness and elasticity, and the amount of zinc can reach 300 grams/square meter. It has the characteristics of thick galvanized layer and strong corrosion resistance. Galvanized iron wire can be cut off in the construction of the tie wire, the length of 20cm, 30cm and 40cm, can be cut off according to requirements.Enclosure to calculate the use of barbed rope, so as to reasonably plan to purchase the amount of barbed rope to facilitate construction.
Hot dip galvanized coating is also relatively thick, but there is an uneven situation, for example, the thickness of the thin is only 45 microns, thick can reach 300 microns or even thicker, the color of this product is relatively dark. There is also a lot of zinc consumed in the production process. Zinc will form an infiltration layer with the metal. Its advantage is that it has good corrosion resistance. Electrogalvanizing, it is through the plating tank in the zinc one-way plating on the outside of the metal products, this way of making products is relatively slow, but its thickness is more uniform.
Cats are agile and good at jumping. Eat fish, rats, rabbits, birds, etc. The reason why cats like to eat fish and mice is because cats are nocturnal animals. In order to see things clearly at night, they need a lot of taurine, and mice and fish contain taurine, so cats are not only because they like eating They eat fish and rats, and they eat because of their own needs. Since cats are widely raised, the market prospect of cat cages is very promising.
Hot dip galvanizing is in the hot melt zinc liquid dip plating, production speed, thick but uneven coating, the market allows the low thickness of 45 microns, up to 300 microns above. It is dark in color, consumes more zinc metal, forms infiltration layer with base metal, and has good corrosion resistance. Hot dip galvanizing can be maintained for decades in outdoor environment.
If the requirements are not high, and the ventilation is good, and relatively dry place, it is recommended to use electric galvanized barbed rope, because the price of this product has a certain advantage, for ordinary users, this is a more appropriate product.Environmental factors should be considered when choosing the thickness of galvanized layer. Galvanized wire in galvanized, pay attention to the above problems, can be well galvanized, to ensure the quality of galvanized wire. Galvanized methods are mainly divided into two types, one is hot dip galvanizing method, the other is electric galvanizing method. This paper mainly introduces the method of galvanizing. Electrogalvanizing is an electrolyte used for galvanizing.
Small and medium-sized cat cages, dog cages and fences are mostly made of pure iron wire, wire diameter is generally between 2-5mm. Of course, the larger the cage, the thicker the wire, because the larger cage needs to withstand more force.
Three methods of twisting the thorn rope: forward twisting, reverse twisting, reverse twisting.
Generally, due to wet weather and more precipitation, oxidation and rust of binding iron wire NetEase occurs, so we should better store and use galvanized iron wire to avoid rust as far as possible. About the barbed wire, the surface of the barbed wire attached a layer of galvanized layer, the galvanized layer if too thick will not meet the SGS environmental standards. But if it is too thin, it is easy to oxidize with water molecules and rust.
It helps to dissipate heat. Building grid (floor heating) has good thermal conductivity and heat dissipation, the appearance of heat dissipation effect is more average 2 cm, 2.5 cm, 5 cm, 10 cm, 15 cm, 20 cm. Wire rope thickness, net length, net width, mesh and other indicators can be stopped at any time according to customer request. The mesh surface, solder joint and mesh are all equal. 5, do not pull the wire beyond the plastic limit.Galvanized iron wire will rust, mainly and the thickness of galvanized layer and the use of the environment, galvanized iron wire is also divided into cold galvanized iron wire and hot galvanized iron wire, in general, hot galvanized iron wire galvanized layer is thicker, rust prevention time is longer, generally can be 7 or 8 years without rust. If the galvanized layer is damaged, or long-term use in a humid environment, it will accelerate the rust time of galvanized iron wire.
Because of the corrosion resistance of zinc layer, can be applied to all kinds of environment, it is also very convenient to use, has been a more popular hardware products. Galvanized iron wire should pay special attention to the acyl wash, to slowly into the container, to prevent acid sputtering on the body, at the same time prohibit the water into, so it is easy to let the acid out, to learn to handle lightly, stacking should also be firm and neat. It can be widely used in construction, handicrafts and other daily civilian applications.
If the coating roughness is not caused by the above reasons, it may be caused by impurities in the plating solution. Can take a small amount of electroplating solution, after filtration test, then take a small amount of electroplating solution, after zinc powder treatment test, check the problem is caused by solid particles or copper, lead and other foreign metal impurities. Test them one by one and it’s not hard to find the cause of the problem. Galvanized iron wire coating foaming, binding force is not good.
The acceptance of cold-drawn low carbon steel wire shall be conducted according to the same production unit, the same raw material, the same diameter, and shall not exceed 30T for an inspection lot, and check the base material into the factory or out of the inspection statement. The inspection items for each inspection lot are appearance quality, diameter error, tensile test (including tensile strength and elongation) and repeated bending test.