Cold galvanizing is in the plating tank through the current unidirectional zinc gradually plated on the metal appearance, the production speed is slow, uniform coating, thin thickness, usually only 3-15 microns, bright appearance, smooth, high aesthetics, poor corrosion resistance, generally a few months will rust. Hot dip galvanized coating is thicker, generally 30-60 microns, coating corrosion resistance is higher. Suitable for outdoor work of steel parts, such as highway fences, power towers, large size fasteners and other more “rough” workpiece long-term rust prevention.
Galvanized hexagonal mesh uses: building wall fixed, heat preservation, heat insulation; Power plant piping, boiler heating; Anti-freezing, residential protection, landscaping protection; Raise chicken and duck, isolate chicken and duck house, play the role of protecting poultry; Protect and support seawalls, hillsides, roads and Bridges and other waterworks.
The impregnated hexagonal wire mesh will lose its original characteristics after corrosion, and will change in shape, color and mechanical properties, resulting in equipment damage, pipeline leakage, etc., specifically, it is easy to break and lose the original protection function. Usually there are three kinds of metal corrosion: physical corrosion, chemical corrosion, electrochemical corrosion, corrosion in addition to the chemical properties and organizational structure of the metal itself, but also related to the surrounding medium, such as wet environment than dry environment easy corrosion, more impurities than impurities less easy corrosion, high temperature conditions than low temperature conditions easy corrosion. After understanding these, we can effectively prevent the corrosion of impregnated hexagonal wire mesh, prolong the service life of products.
The steel mesh is also called longitudinal reinforcement and transverse reinforcement. The longitudinal reinforcement and transverse reinforcement are spaced at right angles to each other, and all the crossing points are welded together. It has the characteristics of crack – proof, small error and good quality. Steel mesh is mainly used in coal mine roadway, concrete pavement, bridge deck, airport runway and buildings. So, what are the advantages of mesh?
In use, there is no need for daily maintenance and maintenance, not only can save a lot of time, but also can reduce costs, but also has good stability, strong corrosion resistance, greatly prolong the service life. According to the different process is divided into different types, can choose according to their own needs. With good flexibility and elasticity, the main role of annealing wire is to control its degree of softness and hardness, in the production of annealing wire is made of steel wire, now more used in the construction industry binding use, compared with ordinary wire is also more soft, have better luster.
The main difference is carbon content. Iron has a carbon content of 2.11 percent or more, while steel has a carbon content of 2.11 percent or less. Iron-carbon alloys with carbon content of more than 2.11% are cast iron (pig iron), which are basically not malleable and cannot be drawn into wire. Secondly, the content of impurities is different, and the content of harmful impurities such as sulfur and phosphorus in steel is smaller. Wire general color key, wire color light point, white point.
However, because the bath contains highly toxic cyanide, the gas escaping from the electroplating process will do great harm to the health of workers, and its waste water must be strictly treated before discharge. Galvanized iron wire has good anti-corrosion and anti-rust ability, so it can be used in some outdoor guardrails or fences, especially on handicrafts, which are also of great use. Galvanized iron wire is not easy to rust and oxidation on the surface.
If the zinc coating is good, but in 3% nitric acid when the light, the coating has dark shadow, passivation occurs when the film is brown, may be caused by foreign metal impurities such as copper or lead in the galvanizing liquid. When problems occur in the process of galvanizing large coil galvanized wire, the temperature and current density are checked first, and then the content of zinc and sodium hydroxide in the plating solution is measured and adjusted through the analysis of the plating solution. Whether DPE content is low can be determined by hull cell test.
The invention technology is used to put zinc block into the plating aid pool regularly, so that the bivalent iron in the plating aid becomes trivalent iron, and plays an important measure to stabilize the PH value within a numerical range, and also facilitate the filter filter out the trivalent iron ions in the plating aid; Ferric ion is controlled between 0.3 and 1.0g/L; When hydrogen is not released in the plating aid, the zinc block is continued. It is an effective measure to reduce zinc slag, improve the fluidity of zinc liquid and reduce the thickness of zinc layer to play the role of plating aid filter.