Wire factory introduction annealing wire is widely used mainly because it has good elasticity and flexibility, in the process of annealing can be very good control of its soft and hard degree, it is mainly made of iron wire, more often used in the construction industry tied wire use. In the production of annealing wire will be processed according to the performance of the material, according to the demand for different degree of hardness of its soft change, can make it has more advantages, can reduce the consumption of metal, reduce the cost of production.
Dip plastic hook net disposal characteristics and downwind, dip plastic is also a common comparison, surface treatment color comparison is single, generally dark green, however, if you want to change into other colors, dip plastic will be more convenient. Because its inner line or inner tube is generally iron line, so, after a period of time, the inner line or inner tube will slowly corrode outward, compared to the outside of the glue fade, hook net will die.
Widely used in practice, iron wire also has certain harm, simple rust and corrosion, so we can generally use galvanized method to prevent product corrosion. Together in addition to this method, metal commonly used treatment methods and phosphating treatment, oxidation treatment, etc. Metal phosphating treatment: iron and steel products to remove oil, rust, into the specific composition of the salt solution soak, you can form a layer of water soluble salt film on the surface of the metal, this process is called phosphating treatment.
The use of galvanized anticorrosion treatment is better, the metallurgical connection between galvanized layer and steel, combined with the appearance of steel as a whole, making the coating more durable, more reliable. In the suburbs, the galvanized thickness of hot dip galvanized can adhere to more than 50 years without repair, in the suburbs or near the seaside, galvanized layer can adhere to more than 20 years without repair, is the choice of anti-rust and anti-corrosion. Coating has strong toughness, in the process of transportation or use, can resist extrusion, withstand some damage, hot dip galvanized anticorrosion treatment both save time and effort, and faster than other processing, than dipping, spraying to save much time and effort.
Black iron wire application in the process, the main is through the hot metal billet rolling into six point five mm wire rod, and then put it in the drawing into a line of different diameter, the plant and then gradually narrow drawing plate aperture, cooling and annealing, plating process, such as making a variety of different specifications of the wire, the wire compared with ordinary black iron wire, will be more softer, Softness is also very uniform, color is also consistent, widely used in the construction industry, mining, chemical industry, welding mesh, welding coat hanger, reprocessing industry and so on.
The error of construction welding net diameter should be controlled at 0.02 mm. For example, we buy wire diameter of 89 wire welding net, with a micrometer to measure the diameter, the diameter of the allowable range is 87 -91 wire. In this range is qualified welding net. Because the accuracy has been compared, but no one can control it so well in the production process. The welding net can be accurate to 0.01 mm, so the error is allowed.
Good galvanized wire, plating thickness of 3- 4 mm, zinc adhesion should be less than 460 grams/m, that is, the average thickness of zinc layer is not less than 65 microns. When the thickness of plated parts is greater than 4 mm, the zinc adhesion should not be less than 610 g/m, that is, the average thickness of zinc layer should not be less than 86 microns. Standard galvanized wire coating must be uniform, galvanized layer basically uniform with copper sulfate solution test etching five times no dew iron. For standard galvanized wire coating adhesion requirements, the zinc layer of plated parts should be firmly combined with the basic metal and have enough adhesion strength, after hammer test does not fall off, not convex.
Every time galvanized wire production enters the peak season of the industry, the road leading to the factory will see from time to time transport wire and container vehicles, as well as galvanized bright wire short-distance transport trucks, driving the labor utilization rate in the surrounding countryside, solving the employment problem of most people. Galvanized wire is divided into hot dip galvanized wire and cold galvanized wire difference: hot dip galvanized is in the heated melting zinc liquid dip plating, production speed is fast, the coating is thick but not uniform. Dark color, consumption of zinc metal, and matrix metal formation of infiltration layer, good corrosion resistance, hot dip galvanizing in outdoor environment can be maintained for decades.
1, zinc pot workers to resolutely do duty and responsibility. Do not leave the post without permission, always observe the change of steel wire galvanized layer, and according to the analysis of the results, master asbestos block gap friction need how long to press, replace the pressing face; Adjust the working face; Until the four faces of the asbestos block are used up, maintenance workers continue to use it after repair when necessary to reduce the consumption of asbestos block.
Hot dip galvanized hexagonal net is made of low carbon steel wire by mechanized braided welding and then by hot dip zinc treatment. The net color is white and shiny, thick zinc layer, uniform mesh, flat mesh surface, solder joint tension resistance, high corrosion resistance. The surface of the steel wire is usually protected by hot-dip galvanizing, and the thickness of the galvanized protective layer can be made according to the requirements of customers. Hot-dip galvanizing hexagonal net is another kind of twisting mesh corresponding to the galvanizing hexagonal net.